Mine resin anchoring agent, fast slow anchoring agent 
 The company produces high-strength anchor agent dedicated unsaturated polyester resin with marble powder, accelerators and accessories, by a certain percentage from the preparation of clay-like bonding material, clay and hardener split with a special polyester film was two-component packaging drugs roll. This product has a long shelf life, high strength anchor to facilitate the construction and excellent performance. Supporting the use of metal or glass steel bolt in underground engineering, slope support, the equipment, installation of the vertical shaft, connected components of the building, equipment foundation anchoring, etc. has been widely used. Is the best anchoring material in the modern anchor engineering. 
 . Classification 
 Product Classification (Table 1). 
 Type characteristics of the gel time / S waiting time / S color-coded 
 Cka super fast 8-25 10-30 Yellow 
 Of CK 8-40 10-60 Red 
 K fast 41-9090-180 blue 
 Z medium speed 91-180480 White 
 M Slow> 180 - 
 Note: The determination of the ambient temperature (22 ± 1) ° C 

 3. Product Specifications: 
 Product specifications (Table 2) 
 Diameter of the anchoring agent resin bolt 352 825 
 The application of the bolt hole diameter of 423 228 
 Note: users with special needs, the resin bolt anchoring agent can produce other specifications, the length of the resin bolt anchoring agent supply and demand sides agreed 

 Two. The main technical parameters of bolt anchoring agent 
 Resin bolt anchoring agent parameters (Table 3) 
 Performance indicators 
 Compressive strength of end anchor ≥ 60MPa 
 Full bolt ≥ 40MPa 
 Consistency (22 ± 1) 0C ≥ 16mm 
 Size deviation of diameter deviation: ± 0.5mm 
 Length deviation: ± 10mm 
 Gel time are shown in Table 1 
 Validity period of 20-25 ℃, indoor storage of ≥ 3 months 
 80 ° C thermal stability test ≥ 16h 



 Anchorage force specified value (Table 4) KN 
 Type CKa CK K, Z-M- 
 Age / min, 15 30 3 10 - 
 Rebar rod body 
 σS ≥ 335MPa Φ22min> 125 
 Φ20min> 105 
 Φ18min> 85 
 Φ16min> 75 

 Round steel rod 
 σS ≥ 235MPa 
 Φ22min> 90 
 Φ20min> 70 
 Φ18min> 60 
 Φ16min> 50 

 Product storage and transportation: 

 A resin anchoring agent should be below 25 ℃, no sunshine drying, indoor storage away from the fire source. 
 Below 25 ℃ storage period of six months, continue to use expired products can be by check soft to the touch. 
 (3) the packaging of the anchor agent rigid carton, plus woven strapping, handling attention to light, to prohibit wrestling whipped. 
 . Rail transport, mutatis mutandis, two flammable materials handling vehicle or LTL motor transport to prevent rain and exposure. 

 Packing: Color coated cardboard boxes.